Mechanical Properties of Hot Rolled Ribbed and Plain Steel Rods
Loading...
Files
Date
2021
Authors
Journal Title
Journal ISSN
Volume Title
Publisher
University of Port Harcourt
Abstract
This study focuses on microstructure and mechanical behaviour of 3PS (Semi-killed mild steel) hot rolled ribbed and plain carbon steel. 3PS billet steel samples and hot rolled ribbed and plain steel rods of different heat umbers and profiles were characterized for its chemical composition, microstructure, and tensile behaviour. The composition analysis of 5 (five) 3PS billet samples shows that there was no appreciable variation in chemical composition of the hot-rolled plain and ribbed steel rods. The microstructures of as-received steel billet (3PS) examination revealed large grains of ferrite and pearlite while those of hot-rolled 3 PS mild steel samples of different heat numbers contain
smaller grains of ferrite and some amount of pearlite. The results also indicated that yield and ultimate tensile strength reach maximum values (492 and 361 N/mm2) at 0.31% elongation for heat number 43 while maximum values for heat number 56 (478 and 362 N/mm2) at 0.33 % respectively. The ribbed steel rod of the same diameter as plain steel exhibit slightly better mechanical properties with higher values of yield and ultimate tensile strength. There is consistency in the chemical composition of the as-received billet and the hot rolled products.
Description
Keywords
Citation
10. Shuaib M. A, Ajao K. R and Oladosu, K.O 2021 Mechanical Properties of Hot rolled Ribbed and Plain Steel Rods J. Appl. Sci. Environ. Manage